Performance index of reinforcement products

Item performance

Test condition

Test method

Data unit

Product designation

2110G

2120G

2130G

2130GB

2710G

2720G

Mechanical property

Tensile strength

23℃ (dry state)

ISO527

MPa

90

     140

160

150

105

150

Elongation at break

23℃ (dry state)

ISO527

%

6

7

7

7

7

9

Bending strength

23℃ (dry state)

ISO178

MPa

130

185

200

180

130

180

Flexural modulus

23℃ (dry state)

ISO178

GPa

2

3

4

4

2

3

Non-notched impact strength

23℃ (dry state)

ISO179

KJ/m2

40

50

50

45

40

65

Notch impact strength

23℃ (dry state)

ISO179

KJ/m2

10

16

15

12

10

16

Glass fiber content

Dry state

ISO3451

%

10

20

30

30

10

20

Physical performance

Specific gravity

Dry state

ISO1183

g/cm3

1.18

1.27

1.35

1.35

1.18

1.27

Molding shrinkage

Dry state

 

%

---

---

---

---

---

---

Thermal performance

Melting range

Dry state

ISO3146

257-262

245-258

245-256

245-256

257-262

245-258

Thermal deformation temperature

1.8Mpa

ISO75

245

245

247

247

245

245

Electrical performance

Dielectric strength

Dry state

GB/T1408

MV/m

---

---

---

---

---

21

Volume resistivity

Dry state

GB/T1410

Ω.cm

1014

1014

1014

1014

1014

7.8×1014

Other

Water absorption

 

 

%

---

---

---

---

---

---

Flame retardant property

Dry state

UL94

 

HB

HB

HB

HB

HB

HB

 

Notes: the data is for reference only. Please consult our material engineers about specific use.

Item performance

Test condition

Test method

Data unit

Product designation

2730G

2730GB

2735G

2750G

L2730G

L2730GH

Mechanical property

Tensile strength

23℃ (dry state)

ISO527

MPa

175

     155

190

230

190

190

Elongation at break

23℃ (dry state)

ISO527

%

8

7

8

7

6

6.5

Bending strength

23℃ (dry state)

ISO178

MPa

210

200

240

300

290

290

Flexural modulus

23℃ (dry state)

ISO178

GPa

5

5

5

8

8

8

Non-notched impact strength

23℃ (dry state)

ISO179

KJ/m2

105

60

100

110

105

105

Notch impact strength

23℃ (dry state)

ISO179

KJ/m2

25

15

20

25

20

20

Glass fiber content

Dry state

ISO3451

%

30

30

35

50

33

33

Physical performance

Specific gravity

Dry state

ISO1183

g/cm3

1.35

1.35

1.35

1.45

1.35

1.35

Molding shrinkage

Dry state

 

%

---

---

1.0-1.5

---

---

---

Thermal performance

Melting range

Dry state

ISO3146

245-260

245-260

256-262

255-265

257-262

258-265

Thermal deformation temperature

1.8Mpa

ISO75

250

245

247

247

254

258

Electrical performance

Dielectric strength

Dry state

GB/T1408

MV/m

18

17

22

23

---

---

Volume resistivity

Dry state

GB/T1410

Ω.cm

1014

1014

1014

1014

1014

1014

Other

Water absorption

 

 

%

---

---

---

---

---

---

Flame retardant property

Dry state

UL94

 

HB

HB

HB

HB

HB

HB

Notes: the data is for reference only. Please consult our material engineers about specific use.